DimensionsYusoff, N. and Ismail, M.C. (2023) Stress Corrosion Cracking and Oxide Layer Growth of P91 Steel in High Temperature Steam Environment. Lecture Notes in Mechanical Engineering. pp. 831-838. ISSN 21954356
Full text not available from this repository.Abstract
The cracking of ferritic alloy steel SA213 P91 materials has been analysed.Environmental factors such as chloride, pH, temperature and dissolved oxygen content in steam may contribute to the propagation of corrosion and SCC cracks on ferritic alloy steel SA213 P91 materials.The SCC crack propagation on P91 alloy will increase with an increase of high chloride content, low pH value, high steam temperature and low oxygen concentration.The remaining steel life also was increase with an increase of oxygen level in test environment. © 2023, Institute of Technology PETRONAS Sdn Bhd.
| Item Type: | Article |
|---|---|
| Additional Information: | cited By 0; Conference of 7th International Conference on Production, Energy and Reliability, ICPER 2020 ; Conference Date: 14 July 2020 Through 16 July 2020; Conference Code:284729 |
| Uncontrolled Keywords: | Alloy steel; Chlorine compounds; Cracks; Dissolved oxygen; High temperature corrosion; Nuclear fuels; Steam; Steel corrosion; Steel metallurgy; Stress corrosion cracking, Chloride contents; Cracks propagation; Dissolved oxygen contents; Environmental factors; Ferritic alloys; Highest temperature; Oxide layer growth; P91 steel; SCC crack; Steam corrosion, Ferrite |
| Depositing User: | Mr Ahmad Suhairi UTP |
| Date Deposited: | 04 Jun 2024 14:11 |
| Last Modified: | 04 Jun 2024 14:11 |
| URI: | https://khub.utp.edu.my/scholars/id/eprint/19521 |
Actions (login required)
- View Item