%T Formation of nano-scale FeCO3 protective corrosion product in carbon dioxide-saturated 3 sodium chloride solution
%P 3-8
%X Corrosion of carbon steel in CO2 saturated NaCl solution contains the formation of FeCO3, as a corrosion product. The protective property of the formed FeCO3 scale layer to corrosion in brine solutions containing CO2 was established as the possible cause of the corrosion rate decrease above 60 °C. In this study, formation of nano-scale FeCO3 film as a corrosion product of X52 carbon steel in CO2-Saturated 3 NaCl solution was investigated. Result showed that corrosion rate decreased after precipitation and formation of protective FeCO3 film in high temperature and high bulk solution pH. © 2017 Trans Tech Publications, Switzerland.
%K Carbon dioxide; Carbon steel; Corrosion protection; Corrosion rate; High temperature corrosion; Manufacture; Nanotechnology; Sodium alloys; Sodium chloride; Steel corrosion, Bulk solutions; CO2 corrosion; Corrosion products; FeCO3; High temperature; Nano scale; Protective properties; Sodium chloride solution, Iron alloys
%R 10.4028/www.scientific.net/KEM.740.3
%D 2017
%L scholars9225
%J Key Engineering Materials
%O cited By 7; Conference of 2nd International Conference on Mechanical, Manufacturing and Process Plant Engineering, ICMMPE 2016 ; Conference Date: 23 November 2016 Through 24 November 2016; Conference Code:195589