<> "The repository administrator has not yet configured an RDF license."^^ . <> . . . "Synthesis of ZnFe2O4 Using sol-gel Method: Effect of Different Calcination Parameters"^^ . "This study aims to synthesize a low band gap semiconductor that will able to convert higher band gap semiconductor under visible light driven photocatalyst. P-type Zinc ferrite (ZnFe2O4) particles were synthesized by a sol-gel method in acidic medium. A stoichiometric amount of zinc nitrate (Zn (NO3)2.4H2O) and ferric nitrate (Fe (NO3)3.9H2O were used. Thermogravimetric analysis (TGA) was performed to study a weight loss at higher temperatures and UV - VIS to determine the minimum wavelength of lightrequired for the activation of the synthesized catalyst. TGA illustrated that maximum weight loss occurs in the temperature range 200-700 °C. When thetemperature exceeded 870 °C, no further decomposition of sample occurred. Absorbance pattern of ZnFe2O4 synthesized under two different conditions (i.e. under N2 gas atmosphere and under normal atmosphere) showed a similar absorbance pattern in wavelength ranges from 380-590 nm but from 590-800 nm, the sample calcined under N2 gas environment exhibits higher absorbance than the sample calcined under atmosphere condition. © 2016 The Authors."^^ . "2016" . . "148" . . "Elsevier Ltd"^^ . . . "Procedia Engineering"^^ . . . "18777058" . . . . . . . . . . . . . . . . . . . "M.S."^^ . "Shaharun"^^ . "M.S. Shaharun"^^ . . "M."^^ . "Khan"^^ . "M. Khan"^^ . . "M.I.A."^^ . "Mutalib"^^ . "M.I.A. Mutalib"^^ . . "F."^^ . "Iqbal"^^ . "F. Iqbal"^^ . . "B."^^ . "Abdullah"^^ . "B. Abdullah"^^ . . . . . "HTML Summary of #7483 \n\nSynthesis of ZnFe2O4 Using sol-gel Method: Effect of Different Calcination Parameters\n\n" . "text/html" . .