N2  - Intumescent Fire retardant coatings (IFRC's) are one of the simplest ways to protect substrates exposed to fire. In this study, Wollastonite (W) filler of two different particle sizes were used to determine the fire performance of intumescent fire retardant coating. The basic ingredients of the coating were ammonium poly-phosphate (APP) as acid source, expandable graphite (EG) as carbon source, melamine (MEL) as blowing agent in epoxy binder, boric acid as additive and hardener as curing agent. A series of coating formulations were developed by using different weight percentages of both sized Wollastonite fillers. The coated steel substrate samples were tested for fire performance using Bunsen burner and char expansion was measured using furnace fire test. A Comparison of the coatings thermal performance was determined. Wollastonite containing filler particle size 10 μm showed better thermal performance than formulations containing filler's particle size 44 μm. © 2014 Owned by the authors, published by EDP Sciences.
VL  - 13
N1  - cited By 1; Conference of 4th International Conference on Production, Energy and Reliability, ICPER 2014 ; Conference Date: 3 June 2014 Through 5 June 2014; Conference Code:106620
KW  - Blowing agents; Coatings; Flammability testing; Hardening; Particle size; Silicate minerals; Substrates
KW  -  Coating formulations; Different particle sizes; Expandable graphite; Filler particles; Fire performance; Intumescent fire retardant coatings; Thermal Performance; Weight percentages
KW  -  Fillers
SN  - 2261236X
TI  - The effect of particle size of wollastonite filler on thermal performance of intumescent fire retardant coating