%K Characterization; Morphology; Synthesis (chemical), Crystallinities; Hydrothermal growth; Pre-Treatment; Pretreatment methods; Structure and morphology; Synthesis durations; Ultrasonic pretreatment; Zeolite T, Hydrothermal synthesis
%I Trans Tech Publications Ltd
%D 2014
%A I.B.M.A. Wahab
%A Y. Fong Yeong
%L scholars4744
%P 911-915
%X In the present work, the lengthy synthesis duration of zeolite-T was successfully reduced by inducing the ultrasonic pre-treatment method prior to hydrothermal growth. The effect of ultrasonic pre-treatment durations on the formation of zeolite-T was investigated. The structure and morphology of the resultant samples were characterized by FTIR, XRD and FESEM. As verified by FTIR, samples produced using synthesis durations of 5, 4, 3 and 2 days with ultrasonic pretreatment durations of 60 min and 90 min, respectively, demonstrated zeolite-T structure. One day synthesis duration was not sufficient for the formation of zeolite-T. From the results obtained by XRD and FESEM, it was found that samples underwent 60 min ultrasonic pre-treatment produced zeolite-T with higher crystallinity, while no significant changes on the morphology of the resultant zeolite-T synthesized using ultrasonic pre-treatment durations of 60 min and 90 min. © 2014 Trans Tech Publications, Switzerland.
%O cited By 5; Conference of 3rd International Conference on Process Engineering and Advanced Materials, ICPEAM 2014 ; Conference Date: 3 June 2014 Through 5 June 2014; Conference Code:114811
%T Effect of ultrasonic pre-treatment durations on the formation of zeolite-T
%V 625
%R 10.4028/www.scientific.net/AMM.625.911
%J Applied Mechanics and Materials