N2  - Glass Fibre Reinforced Polymer (GFRP) gratings are normally manufactured by moulding and pultrusion process. It may consist of various combinations of glass fibre and resin. Even though GFRP gratings have been used widely in normal environment, the use of it in offshore is lacking due to the uncertainty associated with the durability and strength performance. In this paper, a total of twelve GFRP gratings, divided into two groups of moulded and pultruded were tested to failure in flexure. It consists of glass fibres bonded with vinyl ester, polyester and phenolic resin. Prior to the flexural tests, half of the specimens were submerged in synthetic seawater at an elevated temperature of 60 °C for the period of 2 months and the other half was left at room temperature. The results show that most of the submerged gratings experienced strength degradation with varying percentage of reduction. The modes of failure were observed in flexure and shear.
Y1  - 2014///
TI  - Effect of accelerated ageing process on the strength of moulded and pultruded GFRP gratings
KW  - Fiber reinforced plastics; Glass fibers; Polyester resins; Pultrusion; Resins
KW  -  Accelerated ageing process; Elevated temperature; Glass fibre reinforced polymers; Modes of failure; Pultrusion process; Strength degradation; Strength performance; Synthetic seawater
KW  -  Glass
UR  - https://www.scopus.com/inward/record.uri?eid=2-s2.0-85067725672&partnerID=40&md5=594aa7270ff8f326bf85eff362f30bfd
N1  - cited By 0; Conference of 7th International Conference on FRP Composites in Civil Engineering, CICE 2014 ; Conference Date: 20 August 2014 Through 22 August 2014; Conference Code:110944
A1  - Habib, A.I.
A1  - Akbar, I.
ID  - scholars4468
PB  - International Institute for FRP in Construction (IIFC)
AV  - none
ER  -