TY  - JOUR
Y1  - 2014///
VL  - 845
A1  - Maoinser, M.A.
A1  - Ahmad, F.
A1  - Sharif, S.
JF  - Advanced Materials Research
UR  - https://www.scopus.com/inward/record.uri?eid=2-s2.0-84891525966&doi=10.4028%2fwww.scientific.net%2fAMR.845.960&partnerID=40&md5=783f8a0db180f347e941b9db693e3834
CY  - Johor Bahru
ID  - scholars4450
KW  - Aerospace and automotive industries; Drilling quality; Fiber-reinforced-polymeric; Glass and carbon fibers; High-spindle speed; Mechanical fastening; Scanning electron microscopic; Surface roughness (Ra)
KW  -  Automotive industry; Carbides; Carbon fibers; Composite materials; Damage detection; Drilling; Failure (mechanical); Glass; Industrial engineering; Industrial research; Surface roughness; Turning
KW  -  Polymers
KW  -  Carbides; Carbon Fibers; Composites; Damage; Detection; Drilling; Glass; Industrial Engineering; Polymers
N2  - The demand for mechanical fastening in composite materials is increasing due to their potential in large assemblies, aerospace and automotive industries. In practice, small components are integrated into large assemblies drilling holes in composite materials. Drilling defect free holes in composite presents many challenges during part assembly and services. This study presents the effects of cutting parameters used for drilling holes in glass fiber reinforced polymeric (GFRP) composites and hybrid fiber reinforced polymeric (HFRP) composites. Both the composites plates of 3 mm thickness were fabricated using a hand lay-up technique for the purpose of evaluating the effects of parameters on the quality of drilled holes. The holes were drilled using a 5 mm solid carbide twist drill at different spindle speed and feed rate. The quality of holes was assessed with respect to damage factor (Fd) and surface roughness (Ra) of the drilled holes. Results showed that the HFRP composite experienced lower damage factor (Fd) as compared to GFRP composite at lowerfeedrate or spindle speed. Scanning electron microscopic (SEM) examination revealed that the occurrence of delamination, fiber pull-out and matrix cracking was accelerated in the drilled holes at high spindle speed and feed rate. © (2014) Trans Tech Publications, Switzerland.
SN  - 10226680
EP  - 965
AV  - none
SP  - 960
TI  - Effects of cutting parameters on hole integrity when drilling GFRP and HFRP composites
N1  - cited By 5; Conference of 1st International Materials, Industrial, and Manufacturing Engineering Conference, MIMEC 2013 ; Conference Date: 4 December 2013 Through 6 December 2013; Conference Code:101778
ER  -