%0 Journal Article
%@ 10226680
%A Borhan, A.
%A Taha, M.F.
%A Hamzah, A.A.
%C Shah Alam, Selangor
%D 2014
%F scholars:4442
%J Advanced Materials Research
%K Activation conditions; Adsorption materials; Environmental-friendly; Field emission scanning electron microscopes; Meso-pores; Nitrogen adsorption desorption isotherms; Nitrogen adsorption-desorption; Wood sawdust, Activated carbon; Adsorption; Adsorption isotherms; Chemical activation; Gas adsorption; Nanoscience; Nitrogen; Wood, Potassium hydroxide, Adsorption; Nitrogen; Potassium Hydroxide; Wood
%P 132-137
%R 10.4028/www.scientific.net/AMR.832.132
%T Characterization of activated carbon from wood sawdust prepared via chemical activation using potassium hydroxide
%U https://khub.utp.edu.my/scholars/4442/
%V 832
%X The preparation of activated carbon from wood-based industry's residue is one of the most environmental friendly solutions of transforming negative-valued wastes to valuable materials. Wood sawdust was first chemically activated using potassium hydroxide, KOH and characterized by nitrogen adsorption-desorption isotherms measured in Micrometrices ASAP 2020 and Field Emission Scanning Electron Microscope (FESEM). By manipulating three different parameters, the optimal activation conditions were found at temperature of 500°C, activation time of 60 min and impregnation ratio of 1:3. Results showed that the BET surface area, total pore volume and diameter of activated carbon were 1876.16 m2 g-1, 0.88 cm3 g-1 and 6.93 nm, respectively. Nitrogen adsorption desorption isotherm analysis proved the existence of mesopores in activated carbon produced, suggesting that it can be effectively used as an adsorption material. © (2014) Trans Tech Publications, Switzerland.
%Z cited By 7; Conference of 2013 International Conference on Nanoscience and Nanotechnology, NANO-SciTech 2013 ; Conference Date: 1 March 2013 Through 4 March 2013; Conference Code:101772