<> "The repository administrator has not yet configured an RDF license."^^ . <> . . . "Influence of preheat flux on the microstructure of 304 stainless steel"^^ . "An experimental investigation had been carried out for heating-only on samples of type 304 stainless steel with oxyacetylene gas flame set to neutral flame with temperature 2700°-3300°C. The flame effect on surface integrity was investigated in terms of hardness test and microstructural characterization. Substrates temperatures were raised to 355°C as well as 550°C while oxyacetylene flame travels at approximate of 74 mm/min along the span of the material. The experimental outcome revealed the microstructures from two examined conditions: Initial grain structures as well as grain structure when flame heated to 355°C has retained austenite crystal structure while flame heating to 5000-550°C revealed chromium carbide precipitates. Within the investigated temperature range of 500°-550°C, preheating was evidently proven to result to sensitization. © (2014) Trans Tech Publications, Switzerland."^^ . "2014" . . "465-46" . . "Applied Mechanics and Materials"^^ . . . "16609336" . . . . . . . . . . . . . . . . "T.L."^^ . "Gintar"^^ . "T.L. Gintar"^^ . . "A.M."^^ . "Abdulrani"^^ . "A.M. Abdulrani"^^ . . "H."^^ . "Fawad"^^ . "H. Fawad"^^ . . "A.U."^^ . "Alkali"^^ . "A.U. Alkali"^^ . . . . . "HTML Summary of #4432 \n\nInfluence of preheat flux on the microstructure of 304 stainless steel\n\n" . "text/html" . .