eprintid: 4139
rev_number: 2
eprint_status: archive
userid: 1
dir: disk0/00/00/41/39
datestamp: 2023-11-09 16:15:48
lastmod: 2023-11-09 16:15:48
status_changed: 2023-11-09 15:57:45
type: conference_item
metadata_visibility: show
creators_name: Soleimani, H.
creators_name: Yahya, N.
creators_name: Latiff, N.R.A.
creators_name: Sabet, M.
creators_name: Guan, B.H.
creators_name: Chuan, L.K.
title: Co-precipitation synthesis of Co2+xFe2+1-xFe2O4nanoparticles: Structural characterization and magnetic properties
ispublished: pub
note: cited By 0; Conference of 3rd International Conference on Fundamental and Applied Sciences: Innovative Research in Applied Sciences for a Sustainable Future, ICFAS 2014 ; Conference Date: 3 June 2014 Through 5 June 2014; Conference Code:112230
abstract: Cobalt ferrite is known as a promising magnetic material for various applications. This metal-ceramic composite (Cox2+Fe1-x2+Fe2O4) was synthesized via co-precipitation route, by varying the Co/Fe ratios (Co/Fe = 0.3, 0.2, and 0). The structures and magnetic properties of nano-composites were analyzed by XRD and VSM. As deduced from the XRD line broadening, the average crystallite size of the samples was found to be in the range of 13.0-15.0 nm and contain fcc structure with smaller lattice constant as the Co/Fe ratios increases. FESEM and TEM images revealed the morphology of the samples, which consist of irregular shapes of diameter in the range of 9.0-15.0 nm. Magnetic properties measurement shows that sample S11 with the highest Co/Fe ratio has the highest value of saturation magnetization (Ms) of 65.23 emu/g. On the other hand, increase in the concentration of cobalt ions improves the remanence magnetization (Mr) and coercivity (Hc) of the same sample to 12.18 emu/g and 238.92 Oe, respectively. It is demonstrated that the higher substitution ratio of cobalt in Cox2+Fe1-x2+Fe2O4 has successfully improve the magnetic properties of the samples. © 2014 AIP Publishing LLC.
date: 2014
publisher: American Institute of Physics Inc.
official_url: https://www.scopus.com/inward/record.uri?eid=2-s2.0-84969796301&doi=10.1063%2f1.4898514&partnerID=40&md5=f5a9461569870fc391942045b7af90fb
id_number: 10.1063/1.4898514
full_text_status: none
publication: AIP Conference Proceedings
volume: 1621
pagerange: 510-515
refereed: TRUE
isbn: 9780735412583
issn: 0094243X
citation:   Soleimani, H. and Yahya, N. and Latiff, N.R.A. and Sabet, M. and Guan, B.H. and Chuan, L.K.  (2014) Co-precipitation synthesis of Co2+xFe2+1-xFe2O4nanoparticles: Structural characterization and magnetic properties.  In: UNSPECIFIED.