<> "The repository administrator has not yet configured an RDF license."^^ . <> . . . "Electrochemical Performance of Cathode LiVOPO4 Doped with Mo and W"^^ . "Molybdenum (Mo) and tungsten (W) substituted LiV0.99X0.01OPO4 (X = Mo and W) compounds were synthesized by impregnation method. The structures of samples were characterized by X-ray diffraction, and their electrochemical properties were studied by using charge-discharge in galavanostatic mode versus Li+/Li. The electrical conductivity of the samples was estimated by using impedance spectroscopy measurement with 2 point probe method at room temperature. Phosphates of composition LiV0.99X0.01OPO4 with 1 Mo and W content in the structure exhibits high intercalation potential of 3.95 V versus Li/Li+. It was found that the electrical conductivity of Mo and W substituted samples at room temperature was improved to 4.8 � 10-6 and 1.5 � 10-5 S.cm-1, respectively. Discharge capacity was also observed for the W doped sample with good retention performance up to 20 cycles at high current density of C/5 (0.4 mA.cm-2). © 2013 The Indian Ceramic Society."^^ . "2013" . . "72" . "2" . . "Transactions of the Indian Ceramic Society"^^ . . . "0371750X" . . . . . . . . . . . . . . . . "S."^^ . "Maitra"^^ . "S. Maitra"^^ . . "M.A."^^ . "Bustam"^^ . "M.A. Bustam"^^ . . "Z."^^ . "Man"^^ . "Z. Man"^^ . . "T."^^ . "Ishihara"^^ . "T. Ishihara"^^ . . . . . "HTML Summary of #3592 \n\nElectrochemical Performance of Cathode LiVOPO4 Doped with Mo and W\n\n" . "text/html" . .