%K Exposure-time; Hydrogen contents; Hydrogen induced cracking; Hydrogen permeation; Initiation and propagation; Linear polarization resistance; Pipeline steel; Sour environment; Weight loss; X70 pipeline steel; X70 steel, Hydrogen; Hydrogen sulfide; Polarization; Scanning electron microscopy; Sulfur determination, Steel pipe
%N 23
%P 2454-2458
%R 10.3923/jas.2012.2454.2458
%T Corrosion investigation of pipeline steel in hydrogen sulfide containing solutions
%U https://khub.utp.edu.my/scholars/2666/
%V 12
%X The hydrogen-induced cracking (HIC) behavior of X70 pipeline steel was studied by means of Linear Polarization Resistance (LPR), hydrogen permeation tests, weight loss and Scanning Electron Microscopy (SEM). In this study, the dissolved HZS was created by chemical reactions in solution. The specimens were immersed into synthetic sea water saturated with HZS. The experimental results showed that the increase of exposure time and HZS concentration leads to an increase of the hydrogen content in X70 steel, which plays a key role in the initiation and propagation of HIC. © 2012 Asian Network for Scientific Information.
%Z cited By 5