%K Alkaline solutions; Concrete samples; Curing condition; External humidity; Geopolymer; Geopolymer concrete; In-situ; Interfacial transition zone; ITZ; Microstructure properties; MIRHA; Polymerization process; Rice husk ash; Strength development, Curing; Fly ash; Geopolymers; Inorganic polymers, Compressive strength
%X The compressive strength development through polymerization process of alkaline solution and fly ash blended with Microwave Incinerated Rice Husk Ash (MIRHA) is described in this paper. Three curing conditions, which are hot gunny curing, ambient curing, and external humidity curing are investigated to obtain the suitable curing condition for cast in situ provision. Fly ash was blended with MIRHA at 3, 5, and 7 to identify the effect of blended mixes to the compressive strength and microstructure properties of geopolymer concrete. Compressive strength results indicated an improvement in the strength development with external humidity curing concrete samples compared to hot gunny curing and ambient curing. Blended mixes also presented better performance than control mixes. Improvement of interfacial transition zone (ITZ) and micro structure in external humidity concrete samples were also identified compared to hot gunny and ambient curing.
%D 2011
%O cited By 8
%J World Academy of Science, Engineering and Technology
%L scholars2364
%T Compressive strength and interfacial transition zone characteristic of geopolymer concrete with different cast in-situ curing conditions
%A M.F. Nuruddin
%A A. Kusbiantoro
%A S. Qazi
%A N. Shafiq
%V 73
%P 431-434