N2  - Supported cobalt is one of the common catalysts used in Fischer-Tropsch synthesis (FTS). Strong electrostatic adsorption (SEA) was employed to synthesize cobalt nano particles supported on silica. Cobalt nitrate was used as the catalyst precursor and non-porous silica spheres, which were synthesized using the modified Stöber method, were used as a catalyst support. Point of zero charge (PZC) for silica was determined using equilibrium pH at high oxide loading (EpHL) method. The optimum pH was determined by measuring cobalt uptake versus pH. High cobalt uptake at basic pH and low cobalt uptake at acidic pH indicates electrostatic interaction between the cobalt complexes in the precursor solution and the hydroxyl group on the support's surface. Catalysts prepared at optimum pH were characterized using TPR, XPS and TEM. TPR shows reduction peak at high temperature (587°C) indicating strong interaction between cobalt and silica support. XPS shows presence of Co2+ species on the surface. TEM images of the Co/SiO2 at 5 wt and 10 wt cobalt loadings show fairly well-dispersed cobalt oxide nano particles on the spherical silica support with narrow particle size distribution. The findings suggest that SEA was deemed a suitable method to prepare supported cobalt catalysts. © (2011) Trans Tech Publications.
ID  - scholars2360
N1  - cited By 6
TI  - Synthesis of cobalt nano particles on silica support using the strong electrostatic adsorption (SEA) method
JF  - Defect and Diffusion Forum
SN  - 10120386
VL  - 312-31
AV  - none
Y1  - 2011///
KW  - Adsorption; Cobalt; Cobalt compounds; Electrostatics; Fischer-Tropsch synthesis; Heat transfer; High temperature operations; Mass transfer; Nanoparticles; Particle size; Particle size analysis; Silica; Transmission electron microscopy; X ray photoelectron spectroscopy; Diffusion in solids
KW  -  Catalyst precursors; High temperature; Point of zero charge; Precursor solutions; Strong electrostatic adsorptions; Strong interaction; Supported cobalt catalyst; Supported on silica
KW  -  Catalyst supports
SP  - 370
A1  - Chee, K.L.
A1  - Mohd Zabidi, N.A.
A1  - Mohan, C.
PB  - Trans Tech Publications Ltd
ER  -