TY  - JOUR
KW  - Alloy steel; Chlorine compounds; Cracks; Dissolved oxygen; High temperature corrosion; Nuclear fuels; Steam; Steel corrosion; Steel metallurgy; Stress corrosion cracking
KW  -  Chloride contents; Cracks propagation; Dissolved oxygen contents; Environmental factors; Ferritic alloys; Highest temperature; Oxide layer growth; P91 steel; SCC crack; Steam corrosion
KW  -  Ferrite
TI  - Stress Corrosion Cracking and Oxide Layer Growth of P91 Steel in High Temperature Steam Environment
SP  - 831
ID  - scholars19521
N1  - cited By 0; Conference of 7th International Conference on Production, Energy and Reliability, ICPER 2020 ; Conference Date: 14 July 2020 Through 16 July 2020; Conference Code:284729
N2  - The cracking of ferritic alloy steel SA213 P91 materials has been analysed.Environmental factors such as chloride, pH, temperature and dissolved oxygen content in steam may contribute to the propagation of corrosion and SCC cracks on ferritic alloy steel SA213 P91 materials.The SCC crack propagation on P91 alloy will increase with an increase of high chloride content, low pH value, high steam temperature and low oxygen concentration.The remaining steel life also was increase with an increase of oxygen level in test environment. © 2023, Institute of Technology PETRONAS Sdn Bhd.
AV  - none
EP  - 838
UR  - https://www.scopus.com/inward/record.uri?eid=2-s2.0-85140710931&doi=10.1007%2f978-981-19-1939-8_62&partnerID=40&md5=7dccfe975d936b966a6f7c1411364447
A1  - Yusoff, N.
A1  - Ismail, M.C.
JF  - Lecture Notes in Mechanical Engineering
SN  - 21954356
PB  - Springer Science and Business Media Deutschland GmbH
Y1  - 2023///
ER  -