title: Study of c-s-h formation of cemented sediment brick
creator: Ean, L.W.
creator: Malek, M.A.
creator: Mohammed, B.S.
creator: Tang, C.-W.
creator: Ng, C.Y.
description: This paper presents an experimental study of chemical structure formation in newly developed sediment bricks. Morphology analysis was conducted by Scanning Electron Microscope (SEM) images to observe morphological structure and amorphous material while mineralogy analysis through Energy Dispersive Spectroscopy (EDS) and X-Ray Diffraction (XRD) to determine amount of the amorphous materials. C-S-H formation that formed a dense material was observed in Mix 4, which made up from 20 weight of sediment-sand, 70 weight of sediment-silt and stabilized by 10 weight of cement content, which was identified to be the best mix in earlier publication 1. Higher content of calcite in Mix 4 shows existance of carbonates that indicates lower C-S-H formation compared to Mix 1, which has higher cement content. Meanwhile, larger amount of SiO2 in Mix 6 does not indicate higher production of C-H-S. This is verified by SEM images whereby unreacted sediments were observed in Mix 6. This study showed that increment of sediment content disturbed the production of hydration products. In addition, C-S-H formation is not solely verified by amount of SiO2, it has to also verify through SEM images since SiO2 can also be the unreacted raw materials. © The Author(s), under exclusive license to Springer Nature Singapore Pte Ltd. 2021.
publisher: Springer Science and Business Media Deutschland GmbH
date: 2021
type: Article
type: PeerReviewed
identifier:   Ean, L.W. and Malek, M.A. and Mohammed, B.S. and Tang, C.-W. and Ng, C.Y.  (2021) Study of c-s-h formation of cemented sediment brick.  Lecture Notes in Civil Engineering, 132.  pp. 501-509.  ISSN 23662557     
relation: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85100714408&doi=10.1007%2f978-981-33-6311-3_58&partnerID=40&md5=2aa02dc4e9f0f9ecb568e21949d4ba5f
relation: 10.1007/978-981-33-6311-3₅₈
identifier: 10.1007/978-981-33-6311-3₅₈