TY  - JOUR
UR  - https://www.scopus.com/inward/record.uri?eid=2-s2.0-85100602178&doi=10.1016%2fj.ijrmhm.2021.105496&partnerID=40&md5=8dea9c3c535f658a98d48b8d60546680
JF  - International Journal of Refractory Metals and Hard Materials
A1  - Nguyen, V.-H.
A1  - Shahedi Asl, M.
A1  - Delbari, S.A.
A1  - Le, Q.V.
A1  - Sabahi Namini, A.
A1  - Cha, J.H.
A1  - Lee, S.-H.
A1  - Jang, H.W.
A1  - Mustapha, M.
A1  - Mohammadi, M.
A1  - Shokouhimehr, M.
VL  - 96
Y1  - 2021///
SN  - 02634368
PB  - Elsevier Ltd
N2  - This examination intended to evaluate the synergic influence of graphene nano-platelets (GNPs) and AlN on the microstructure and consolidation behavior of TiC. The spark plasma sintering (SPS) method was employed as the manufacturing process under the sintering circumstances of 40 MPa, 10 min, and 1900 °C. The simultaneous incorporation of AlN and GNPs could improve the relative density of TiC more than 4, reaching a fully dense ceramic. According to the X-ray diffraction (XRD) spectrum, thermodynamic study, as well as the microstructural assessments, i.e., scanning electron microscopy (SEM), Electron probe micro-analyzer (EPMA), scanning transmission electron microscopy (STEM) and transmission electron microscopy (TEM), the TiN and Al2OC ingredients were produced over the SPS process as the in-situ phases. Although Al2OC remained in the microstructure as an amorphous-like phase, the in-situ produced TiN dissolved into the TiC matrix, creating a Ti(C,N) solid solution. A chemical reaction between AlN and the surface oxide of TiC, namely TiO2, was found to be responsible for the in-situ generation of the TiN compound. Thanks to the formation of the solid solution, strong interfaces were created amongst the matrix grains, promoting the transgranular fracture mode. Moreover, some dislocations and distorted atomic planes were seen in the microstructure, derived from the thermal expansion coefficients' inconsistency between the different phases over the cooling stage. © 2021 Elsevier Ltd
N1  - cited By 3
KW  - Aluminum nitride; Electrons; Graphene; High resolution transmission electron microscopy; III-V semiconductors; Microstructural evolution; Oxide minerals; Scanning electron microscopy; Solid solutions; Spark plasma sintering; Textures; Thermal expansion; Tin oxides; Titanium carbide; Titanium dioxide; Titanium nitride; Transmissions
KW  -  Electron probe micro analyzer; Manufacturing process; Microstructural assessments; Scanning transmission electron microscopy; Spark plasma sintering method; Thermal expansion coefficients; Thermodynamic studies; Transgranular fracture
KW  -  Tin metallography
ID  - scholars15063
TI  - Microstructural evolution during spark plasma sintering of TiCâ??AlNâ??graphene ceramics
AV  - none
ER  -