%A Chong, C.C.
%A Cheng, Y.W.
%A Bukhari, S.N.
%A Setiabudi, H.D.
%A Jalil, A.A.
%D 2021
%F scholars:14556
%I Elsevier B.V.
%J Catalysis Today
%K Catalyst activity; Decomposition; Impregnation; Mass transfer; Methane; Microemulsions; Molecular sieves; Morphology; Nickel oxide; Silica, Metal-support interactions; Methane dry reforming; Microemulsion technique; Molecular sieve materials; Optimal temperature; Reactant conversion; Support morphology; Surface attributes, Nickel
%P 245-257
%R 10.1016/j.cattod.2020.06.073
%T Methane dry reforming over Ni/fibrous SBA-15 catalysts: Effects of support morphology (rod-liked F-SBA-15 and dendritic DFSBA-15)
%U https://khub.utp.edu.my/scholars/14556/
%V 375
%X Santa Barbara Amorphous-15 (SBA-15) is a promising molecular sieve material with its highly uniform porosity; nonetheless, its tubular pore channels discouraged mass transfer of reactants during catalysis. Herein, SBA-15 was altered by microemulsion technique to prepare two fibrous SBA-15 with distinct morphologies, viz. rod-liked F-SBA-15 and dendritic DFSBA-15. After Ni impregnation, the Ni/fibrous SBA-15 catalysts (Ni/F-SBA-15 and Ni/DFSBA-15) were catalytically evaluated with methane dry reforming (MDR). From characterization, rod-shaped F-SBA-15 had outer fibrous layer whereas dendritic DFSBA-15 consisted of a solid core with radially projected fibres. Besides, Ni/F-SBA-15 possessed uneven sized NiO but Ni/DFSBA-15 had uniform NiO dispersion. Characterization also proved that fibrillation and Ni impregnation did not alter the pristine properties of SBA-15. However, the surface attributes of SBA-15 remarkably reduced after fibrillation and Ni impregnation. The strength of metal-support (Ni-SiO2) interaction could be ranked as: Ni/DFSBA-15 > Ni/F-SBA-15 > Ni/SBA-15 (previously reported). Both Ni/fibrous SBA-15 catalysts exhibited high proportion of moderate basicity, which favoured the carbon removal via reverse Boudouard reaction. In accordance with endothermicity, the optimal temperature of MDR over both catalysts was 800 °C as greater temperature provoked conspicuous CH4 thermal decomposition. For 50 h MDR at 800 °C, both catalysts presented superior catalytic activity and stability. With a fully accessible siliceous framework, Ni/DFSBA-15 attained greater reactant conversions (84.05�87.40 XCH4 and 81.80�85.60 XCO2) than Ni/F-SBA-15 (80.30�85.80 XCH4 and 76.73�84.10 XCO2). In overall, Ni/DFSBA-15 was more coke-resistant than Ni/F-SBA-15 by virtue of its fully accessible structure, uniformly dispersed Ni phase, and stronger metal-support interaction. © 2020 Elsevier B.V.