title: Comparative Study on Ni/γ-Al2O3Prepared via Ultrasonic Irradiation and Impregnation Approaches as an Oxygen Carrier in Chemical Looping Combustion
creator: Ghazali, N.A.
creator: Aqsha, A.
creator: Komiyama, M.
creator: Qasim, M.
creator: Mohd Yusoff, M.H.
creator: Ayoub, M.
creator: Ameen, M.
creator: Tijani, M.M.
description: With the recent advancement of the chemical looping combustion (CLC) industry, the development of materials with high stability, high oxidation and reduction rate, and high oxygen transport capacity (OTC) has become a research hotspot. In this paper, the behavior of nickel oxide (NiO) as an oxygen carrier (OC) has been analyzed using thermogravimetric analysis. The influences of the preparation methods and Ni composition have been evaluated to develop Ni-based carriers with high reduction and oxidation rates over 10 redox cycles without changes in the chemical and structural properties. It has been observed that the carriers prepared by the ultrasound irradiation method showed excellent stability and higher reduction and oxidation rate (less than 1-3 min) during multiple redox cycles. However, their OTC values were lower than those of impregnated carriers. It was found that, in the ultrasound irradiation method, the 15NA (15 wt  Ni loading supported with gamma alumina) OC exhibited the highest OTC (3.17) while 5NA (5 wt  nickel loading supported with gamma alumina) exhibited the lowest OTC (1.34). A similar trend was observed for the impregnated OC, where 15NA exhibited the highest OTC value (3.67), whereas 5NA exhibited the lowest OTC value (1.38). Overall, the carriers prepared via the impregnation method possessed a high value of OTC at approximately 3.67 while the carriers prepared by ultrasound irradiation possessed an OTC value of 3.17. In terms of physicochemical properties, the carriers prepared using the ultrasound irradiation approach possessed comparatively lower oxidation and reduction temperatures, smaller particle size, higher specific surface area, and more uniform metal distribution on the support. These findings suggested that the Ni-based OC prepared by ultrasound irradiation is a good candidate for CLC reactions. © 2021 American Chemical Society. All rights reserved.
publisher: American Chemical Society
date: 2021
type: Article
type: PeerReviewed
identifier:   Ghazali, N.A. and Aqsha, A. and Komiyama, M. and Qasim, M. and Mohd Yusoff, M.H. and Ayoub, M. and Ameen, M. and Tijani, M.M.  (2021) Comparative Study on Ni/γ-Al2O3Prepared via Ultrasonic Irradiation and Impregnation Approaches as an Oxygen Carrier in Chemical Looping Combustion.  Industrial and Engineering Chemistry Research, 60 (37).  pp. 13542-13552.  ISSN 08885885     
relation: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85115657108&doi=10.1021%2facs.iecr.1c02485&partnerID=40&md5=0e0e87c69c6a2f16d9b17d1a21c28e1d
relation: 10.1021/acs.iecr.1c02485
identifier: 10.1021/acs.iecr.1c02485