relation: https://khub.utp.edu.my/scholars/12553/
title: Development of hybrid and templated silica�p123 membranes for brackish water desalination
creator: Elma, M.
creator: Mujiyanti, D.R.
creator: Ismail, N.M.
creator: Bilad, M.R.
creator: Rahma, A.
creator: Rahman, S.K.
creator: Fitriani
creator: Rakhman, A.
creator: Rampun, E.L.A.
description: Water scarcity is still a pressing issue in many regions. The application of membrane technology through water desalination to convert brackish to potable water is a promising technology to solve this issue. This study compared the performance of templated TEOS�P123 and ES40�P123 hybrid membranes for brackish water desalination. The membranes were prepared by the sol�gel method by employing tetraethyl orthosilicate (TEOS) for the carbon�templated silica (soft template) and ethyl silicate (ES40) for the hybrid organo�silica. Both sols were templated by adding 35 wt. of pluronic triblock copolymer (P123) as the carbon source. The silica�templated sols were dip�coated onto alumina support (four layers) and were calcined by using the RTP (rapid thermal processing) method. The prepared membranes were tested using pervaporation set up at room temperature (~25 °C) using brackish water (0.3 and 1 wt.) as the feed. It was found that the hybrid membrane exhibited the highest specific surface area (6.72 m2�g�1), pore size (3.67 nm), and pore volume (0.45 cm3�g�1). The hybrid ES40�P123 was twice thicker (2 μm) than TEOS�P123� templated membranes (1 μm). Lastly, the hybrid ES40�P123 displayed highest water flux of 6.2 kg�m�2�h�1. Both membranes showed excellent robustness and salt rejections of >99. © 2020 by the authors. Licensee MDPI, Basel, Switzerland.
publisher: MDPI AG
date: 2020
type: Article
type: PeerReviewed
identifier:   Elma, M. and Mujiyanti, D.R. and Ismail, N.M. and Bilad, M.R. and Rahma, A. and Rahman, S.K. and Fitriani and Rakhman, A. and Rampun, E.L.A.  (2020) Development of hybrid and templated silica�p123 membranes for brackish water desalination.  Polymers, 12 (11).  pp. 1-13.  ISSN 20734360     
relation: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85095968733&doi=10.3390%2fpolym12112644&partnerID=40&md5=279096fd68467edd9648ec335acf35e8
relation: 10.3390/polym12112644
identifier: 10.3390/polym12112644