%X Global warming due to the emission of carbon dioxide (CO2) has become a serious problem in recent times. Although diverse methods have been offered, adsorption using activated carbon (AC) from agriculture waste is regarded to be the most applicable one due to numerous advantages. In this paper, the preparation of AC from rubber-seed shell (RSS), an agriculture residue through chemical activation using potassium hydroxide (KOH), was investigated. The prepared AC was characterized by nitrogen adsorption-desorption isotherms measured in Micrometrices ASAP 2020 and FESEM. The optimal activation conditions were found at an impregnation ratio of 1:2 and carbonized at a temperature of 700 °C for 120 min. Sample A6 is found to yield the largest surface area of 1129.68 m2/g with a mesoporous pore diameter of 3.46 nm, respectively. Using the static volumetric technique evaluated at 25 °C and 1.25 bar, the maximum CO2 adsorption capacity is 43.509 cm3/g. The experimental data were analyzed using several isotherm and kinetic models. Owing to the closeness of regression coefficient (R2) to unity, the Freundlich isotherm and pseudo-second kinetic model provide the best fit to the experimental data suggesting that the RSS AC prepared is an attractive source for CO2 adsorption applications. © 2019 by the authors.
%I MDPI AG
%V 7
%A A. Borhan
%A S. Yusup
%A J.W. Lim
%A P.L. Show
%T Characterization and modelling studies of activated carbon produced from rubber-seed shell using KOH for CO2 adsorption