N2  - This study aims to analyse the effects of carbon nanospheres (CNSs) on the in-plane shear properties of basalt fiber-reinforced epoxy composite laminate (BFR). The CNSs were obtained from an economical fibrous residue attained from the sago palm tree, which is known as biowaste sago bark. Hand lay-up method was used to fabricate the unidirectional basalt fiber-reinforced epoxy composite laminates. The epoxy resin was mixed with carbon nanosphere particles (i.e., 0.6 wt - 1 wt). In-plane shear tests have been conducted as per ASTM standards. In addition, emphasis on the microstructural investigation using Scanning Electron Microscopy (SEM) is given, in order to study the fracture surfaces of the composite laminates. The results demonstrated significant improvement in in-plane shear strength when carbon nanosphere particles were included in the basalt fiber-reinforced epoxy composite laminate. The best result was obtained at 1.0 wt CNSs. It displayed an increment of 37.1 in in-plane shear strength, and 36.4 increment in modulus of rigidity, respectively, in comparison to neat basalt fiber-reinforced epoxy composite laminate. The improved accomplishment of CNSs/basalt fiber-reinforced epoxy composite laminate is due to good distribution of CNSs particles in the epoxy matrix. © 2018 Institute of Physics Publishing. All rights reserved.
N1  - cited By 0; Conference of 1st International Conference on Advances in Engineering and Technology, ICAET 2018 ; Conference Date: 2 April 2018 Through 3 April 2018; Conference Code:139913
TI  - In-plane shear strength analysis of Basalt Fiber-Reinforced Epoxy Laminates with Biowaste Catalyst Free Carbon
ID  - scholars10025
KW  - ASTM standards; Basalt; Carbon; Epoxy resins; Fiber reinforced plastics; Fibers; Laminated composites; Nanospheres; Reinforcement; Scanning electron microscopy; Shear flow; Shear strength; Starch
KW  -  Bio-waste; Composite laminate; Fiber reinforced; Fiber reinforced epoxy composites; In-plane shear properties; In-plane shear strength; Microstructural investigation; Modulus of rigidities
KW  -  Particle reinforced composites
Y1  - 2018///
PB  - Institute of Physics Publishing
SN  - 17578981
A1  - Mengal, A.N.
A1  - Karuppanan, S.
A1  - Qaisarani, Z.N.
A1  - Siddique, M.
A1  - Kashif, M.
A1  - Najam, M.
UR  - https://www.scopus.com/inward/record.uri?eid=2-s2.0-85054275066&doi=10.1088%2f1757-899X%2f414%2f1%2f012031&partnerID=40&md5=93152a5e8bbef22429b60e5f9f6bc544
VL  - 414
ER  -