Recent researches of fire retardant intumescent coatings reinforced by single Rockwool and single glass wool fibre at various weight percentages and lengths showed some improvements to the mechanical properties of the coatings and the char produced. Therefore, in this research the fibres were combined together in intumescent coating formulation at several weight percentages and fibre lengths to study their effects towards fire resistance performance and char morphology. The hybrid fibre reinforced intumescent coatings were subjected to two types of fire tests; Bunsen burner at 1000°C and the electric furnace at 800°C for 1 hour, respectively. Steel temperature of the coated samples during Bunsen burner test was recorded to determine the fire resistance performance. Thermal stability of the intumescent coatings and chars was determined by Thermogravimetric Analysis (TGA). The morphology of the coatings and char was then examined by using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectrometry (EDS) was conducted to obtain elemental composition of the samples. This research concluded that long-hybrid fibre at 12-mm length and 0.6 fibre-weight produced the top performing hybrid fibre intumescent formulation. The hybrid fibres form survived at elevated temperature, hence helped to provide structure and strengthen the char with the highest fire resistance was recorded at steel temperature of 197°C. © Owned by the authors, published by EDP Sciences, 2016.